In fact, there are many glass bottles used in our lives. The most common ones are wine bottles and vases. Although these glass bottles do not have much demand on the quality of consumption, but if you want a better price, then you must be id The appearance must also have good quality.
Glass bottle manufacturers have informed us that in fact, glass bottles are used for many purposes, and glass bottles are also required in hospitals or some laboratories. However, due to different uses, the requirements are different. In order to be more hygienic and safer to use glass bottles ,
It is necessary to stop disinfection, and often stop inspections.
The glass bottles used in the laboratory should be checked regularly, and there should be no damage, so as not to affect the experiment. If the glass bottles are found to be damaged or chipped, they should be removed and not used.
However, if the glass bottle needs to be disinfected after the experiment, so as not to affect the experimental effect in the next use. When disinfecting, pay attention to the glass bottle mouth down, and the sterilized glass bottle should maintain a certain degree of illumination. Inspectors check. Check that there are no abnormal glass bottles and need to be placed in the designated storage location. In order not to affect the use of glass bottles, be careful to handle them with care during the placement and cleaning process.
When the glass bottle is produced, the workers in the team will first look at the general situation of the product, and then after a period of annealing, the workshop director is carefully checking the situation. The general situation is as follows, let us know:
Deformation of the glass bottle body: Because the bottle that the forming mold enters has not been completely shaped, at this time, the droplet temperature and the induction temperature will often cause the glass bottle to collapse and deform. If the upper part of the bottle body is too heavy, it will be like this. Occasionally, the bottom of the bottle is not cooled to a certain temperature, it will be printed with the marks of the conveyor belt, making the bottom of the bottle unyielding.
Glass bottle body traces: Glass bottle manufacturers introduce that traces are the most widespread problem of glass bottles. It can be extremely thin, and some can only be created in reflected light. The parts that often occur are the bottle mouth, neck and shoulders, and there are often traces on the bottle body and bottom, which are caused by the temperature of the furnace.
The thickness of the glass bottle is uneven: Assuming that the glass bottle manufacturer has an uneven temperature of the glass gob during the processing process, the high temperature part has a small viscosity and is easy to blow thin, and the low temperature part has large resistance and thicker. In addition, the mold temperature is not uniform. The glass on the high temperature side cools slowly and is easy to blow thinly, and the lower temperature side is blown thick because the glass cools quickly.
The environment of glass bottle cracks: cracks have various shapes, some are creases, and some are very thin wrinkles. The primary cause is that the gob is too cold, the gob is too long, and the gob does not fall in the center of the prototype It is caused by adhesion on the cavity wall.
Bubble: The bubbles produced by the glass bottle manufacturer during the forming process are often a few large bubbles or how many small bubbles are gathered together, which is different from the uniformly distributed small bubbles of the glass itself.
Post time: 9月-03-2020